Alright, I may be new to sabers and very possible naive, but I figured a battle blade would stand up to drywall. Apparently not my blade though. I have three theories of why it cracked.
1) Not as indestructible as I thought.
2) Flaw/weak point in the polycarbonate that I happened to hit.
3) Since I was unable to locate Weld-On 3, is it possible the good old-fashioned super glue made the polycarbonate brittle, leading to the cracks?
Any thoughts on these or other theories so that when I either cut this blade down past the cracks (blade will be way too short for hilt) or can find the money for new blade supplies (baby on the way), I won't make the same mistake?